| 板材 |
|
852 |
383 |
46 |
|
| 板材* |
固溶退火 |
|
|
|
92 |
| 棒材** |
固溶退火 |
|
|
|
90 |
| 薄板 |
|
837 |
417 |
47.3 |
|
| 薄板；t=3 |
Cold reduction 10%, subsequent anneal at 1066°C (1950°F) |
990 |
635 |
32.9 |
|
| 薄板；t=3 |
Cold reduction 10%, subsequent anneal at 1121°C (2050°F) |
960 |
555 |
36.5 |
|
| 薄板；t=3 |
Cold reduction 10%, subsequent anneal at 1177°C (2150°F) |
895 |
385 |
43.7 |
|
| 薄板；t=3 |
Cold reduction 20%, subsequent anneal at 1066°C (1950°F) |
980 |
555 |
35.6 |
|
| 薄板；t=3 |
Cold reduction 20%, subsequent anneal at 1121°C (2050°F) |
935 |
450 |
39.2 |
|
| 薄板；t=3 |
Cold reduction 20%, subsequent anneal at 1177°C (2150°F) |
925 |
445 |
40.1 |
|
| 薄板；t=3 |
Cold reduction 30%, subsequent anneal at 1066°C (1950°F) |
980 |
525 |
35.7 |
|
| 薄板；t=3 |
Cold reduction 30%, subsequent anneal at 1121°C (2050°F) |
965 |
495 |
37.6 |
|
| 薄板；t=3 |
Cold reduction 30%, subsequent anneal at 1177°C (2150°F) |
950 |
450 |
38.5 |
|
| 薄板；t=3 |
Cold reduction 40%, subsequent anneal at 1066°C (1950°F) |
1005 |
560 |
32.3 |
|
| 薄板；t=3 |
Cold reduction 40%, subsequent anneal at 1121°C (2050°F) |
980 |
525 |
35.5 |
|
| 薄板；t=3 |
Cold reduction 40%, subsequent anneal at 1177°C (2150°F) |
960 |
505 |
38.1 |
|
| 薄板；t=3 |
Cold reduction 50%, subsequent anneal at 1066°C (1950°F) |
1020 |
595 |
34.6 |
|
| 薄板；t=3 |
Cold reduction 50%, subsequent anneal at 1121°C (2050°F) |
990 |
555 |
36.3 |
|
| 薄板；t=3 |
Cold reduction 50%, subsequent anneal at 1177°C (2150°F) |
950 |
495 |
39.1 |
|
| 薄板；t=3 |
冷轧0% |
885 |
425 |
46.6 |
|
| 薄板；t=3 |
冷轧10% |
995 |
715 |
31.8 |
|
| 薄板；t=3 |
冷轧20% |
1130 |
920 |
16.8 |
|
| 薄板；t=3 |
冷轧30% |
1295 |
1105 |
9.7 |
|
| 薄板；t=3 |
冷轧40% |
1390 |
1190 |
7.5 |
|
| 薄板；t=3 |
冷轧50% |
1480 |
1275 |
6 |
|
| 薄板*** |
固溶退火 |
|
|
|
92 |