牌号	A3
对应标准	BS 3100-1991 一般工程用铸钢件 Specification for Steel castings for general engineering purposes
归类	铸钢
标签	碳钢铸钢

A3 化学元素成分含量(%)

成分	C	Si	Mn	P	S
最小值	-	-	-	-	-
最大值	0.45	0.6	1	0.05	0.05

①碳含量每降低0.01%，最大锰含量则增加0.04%，允许最大锰含量到1.1% 碳当量计算

A3 机械性能

热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %	冲击吸收能量 KV2 J
A或N或N+T或OQ+T或WQ+T	≥540	≥295	≥14	≥18

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool. 表中值适用于铸件截面厚度小于等于500mm，超过此尺寸的机械性能应与制造商协商。

近似对照表铸钢

中国	日本	美国		国际标准组织	德国		俄罗斯	英国
GB	JIS	ASTM	UNS	ISO	DIN EN/DIN	W-Nr.	GOST	BS EN/BS
ZG310-570	SCC5	80-40	J05002	340-550	GS-70 GS-CK45	1.0554 1.1191	45Л	A3 AW2