420C29_全球钢材百科网钢材化学成分-热处理-物理性能介绍-全球钢材百科网

420C29简介

牌号	420C29
对应标准	BS 3100-1991 一般工程用铸钢件 Specification for Steel castings for general engineering purposes
归类	铸钢
性能	耐腐蚀
标签	不锈钢铸钢

420C29 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Cu ^①
最小值	-	-	-	-	-	11.5	-	-
最大值	0.2	1	1	0.04	0.04	13.5	1	0.3

①残余元素碳当量计算

420C29 机械性能

热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %
AH+T或OQ+T(T at 750°C max)	≥690	≥465	≥11

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

1 近似对照表耐蚀铸钢（不锈钢铸件）

中国		中国台湾	日本	韩国	美国		德国		法国	俄罗斯	英国
GB	ISC	CNS	JIS	KS	ASTM	UNS	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
ZG20Cr13	C54200	SCS 2	SCS 2	SSC 2	CA40	J91153	GXCr20Ni14	1.4027	Z20C13M	20Х13Л	420C29

2 近似对照表耐蚀铸钢（不锈钢铸件）

中国	日本	德国		法国	俄罗斯	英国
GB	JIS	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
ZG2Cr13Ni	SUS2	G-X20Cr14	1.4027	Z20C 13M	20Х13Л	420C29

3 近似对照表耐热铸钢和耐热合金铸件

中国	日本	美国		德国		法国	俄罗斯	英国
GB	JIS	ASTM	UNS	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
ZG2Cr13	SCS2	CA40	J91153	G-X20Cr14	1.4027	Z20C13M	20Х13Л	420C29