304C15简介

牌号	304C15
对应标准	BS 3100-1991 一般工程用铸钢件 Specification for Steel castings for general engineering purposes
归类	铸钢
性能	耐腐蚀
标签	奥氏体不锈铸钢有磁性

304C15 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni
最小值	-	-	-	-	-	18	8
最大值	0.08	1.5	2	0.04	0.04	21	11

碳当量计算

304C15 机械性能

热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %
ST(1000°C~1100°C)	≥480	1% proof stress Rp1.0 min ≥215	≥26

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

1 近似对照表耐蚀铸钢（不锈钢铸件）

中国

中国台湾

日本

韩国

美国

德国

法国

俄罗斯

瑞典

英国

ISC

CNS

JIS

ASTM

UNS

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

SS₁₄

BS EN/BS

ZG07Cr19Ni9

C53048

SCS 13A

SSC 13A

CF8

J92600

GX5CrNi19-10

1.4308

Z2CN18.10M

07Х18Н9Л

2333

304C15

2 近似对照表耐蚀铸钢（不锈钢铸件）

中国		中国台湾	日本	韩国	国际标准组织	德国		法国	俄罗斯	瑞典	英国
GB	ISC	CNS	JIS	KS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	SS₁₄	BS EN/BS
ZG07Cr19Ni9	C53048	SCS 13	SCS 13X	SSC 13	GX5CrNi19-9	GX5CrNi19-10	1.4308	Z2CN18.10M	07Х18Н9Л	2333	304C15

3 近似对照表耐蚀铸钢（不锈钢铸件）

中国	日本	美国	德国		法国	俄罗斯	英国
GB	JIS	ASTM	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
ZG0Cr18Ni9	SUS13	CF8	G-X6CrNi18 9	1.4038	Z6CN18.10M	07Х18Н9Л	304C15

4 近似对照表耐热铸钢和耐热合金铸件

中国	日本	美国		德国		法国	俄罗斯	英国
GB	JIS	ASTM	UNS	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
ZG0Cr18Ni9	SCS13	CF	J92600	G-X6CrNi18 9	1.4308	Z6CN18.10M Z6CN19.9M	07Х18Н9Л	304C15