310C40简介

牌号	310C40
对应标准	BS 3100-1991 一般工程用铸钢件 Specification for Steel castings for general engineering purposes
归类	铸钢
性能	耐腐蚀
标签	耐热不锈铸钢有磁性

310C40 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Mo
最小值	0.3	-	-	-	-	24	19	-
最大值	0.5	1.5	2	0.04	0.04	27	22	1.5

碳当量计算

310C40 机械性能

热处理或状态	抗拉强度 σ_b Mpa	断后伸长率或延伸率 δ %
As cast	≥450	≥7

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

1 近似对照表耐热铸钢和耐热合金铸件

中国

中国台湾

日本

韩国

美国

国际标准组织

德国

法国

俄罗斯

英国

ISC

CNS

JIS

ASTM

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

BS EN/BS

ZG40Cr25Ni20Si2

C53901

SCH 21

HRSC 21

HK30

J94203

GX40NiCrSi25-20

1.4848

Z40CN25.20M

≈15Х23Н18Л

310C40

2 近似对照表耐蚀铸钢（不锈钢铸件）

中国	日本	美国	德国		英国
GB	JIS	ASTM	DIN EN/DIN	W-Nr.	BS EN/BS
ZG4Cr25Ni20Si2	SCH22	HK40	G-X40CrNiSi2520	1.4848	310C40

3 近似对照表耐热铸钢和耐热合金铸件

中国	日本	美国		德国		英国
GB	JIS	ASTM	UNS	DIN EN/DIN	W-Nr.	BS EN/BS
ZG4Cr25Ni20Si2	SCH22	HK HK-40	J94224 J94204	G-X40CrNiSi25 20	1.4848	310C40 310C45

聚合信息推荐

行业资讯

价格走势

其他信息

宝山钢铁股份有限公司

宝山钢铁股份有限公司（简称“宝钢股份”）是中国最大、最现代化的钢铁联合企业。宝钢股份以其诚信、人才、创新、管理、技术诸方面综合...

打开PDF