GX40CrSi23_全球钢材百科网钢材化学成分-热处理-物理性能介绍-全球钢材百科网

GX40CrSi23简介

牌号	GX40CrSi23
德国W-Nr.	1.4745
对应标准	DIN 17465-1993 耐热铸钢 Heat resisting steel castings - Technical delivery conditions
归类	铸钢
标签	铁素体型耐热铸钢最高工作温度1050°C

GX40CrSi23 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr
最小值	0.3	1	0.5	-	-	22
最大值	0.45	2.5	1	0.035	0.03	24

碳当量计算

GX40CrSi23 机械性能

产品	热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %	硬度 HBW
铸钢	铸态	-	-	-	-

高温性能及最高使用温度

Material 1% creep limit after 10000 h, in N/mm²,
at a temperature, in °C, of Maximum service
temperature,
in °C
designation number 600 700 800 900 1000 1100
GX40CrSi23 1.4745 26 11 5 1.5 - - 1050

物理性能

Material		Den- sity, in g/cm³	Thermal con- ductivity, in W/K.m	Specific heat capacity at 20 °C, in J/g.K	Coefficient of linear thermal expansion, in 10^-6 /K, at a temperature between 20 °C and
designation	number	Den- sity, in g/cm³	Thermal con- ductivity, in W/K.m	Specific heat capacity at 20 °C, in J/g.K	400 °C	800°C	1000°c
GX40CrSi23	1.4745	7.6	18.8	0.50	12.0	14.0	16.0

焊接资料

Material

suitable fillet metal

Heat treatment

designation

number

Covered electrode (symbol)

Wire or rod
(symbol)

Material number

prior to welding

after welding

GX40CrSi23

1.4745

3025 425 20

X8Cr30 X12CrNi25-4 X12CrNi25-20

1.4773 1.4820 1.4842

预热到700~800°C

炉内缓慢冷却

近似对照表耐热铸钢和耐热合金铸件

中国

中国台湾

日本

韩国

美国

国际标准组织

德国

法国

俄罗斯

英国

ISC

CNS

JIS

ASTM

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

BS EN/BS

ZG40Cr24Si2

C54834

SCH 2

SCH 2X1

HRSC 2

J92605

GX40CrSi24

1.4745

GX40CrSi24

15Х25ТЛ

GX40CrSi24

聚合信息推荐

行业资讯

价格走势

其他信息

宝山钢铁股份有限公司

宝山钢铁股份有限公司（简称“宝钢股份”）是中国最大、最现代化的钢铁联合企业。宝钢股份以其诚信、人才、创新、管理、技术诸方面综合...

打开PDF

Material		1% creep limit after 10000 h, in N/mm², at a temperature, in °C, of						Maximum service temperature, in °C
designation	number	600	700	800	900	1000	1100	Maximum service temperature, in °C
GX40CrSi23	1.4745	26	11	5	1.5	-	-	1050

高温性能及最高使用温度

物理性能

焊接资料